NA100 - CARACTERÍSTICAS DO PAPELÃO HIDRÁULICO

[pic 1] 

 

TEADIT NA-1100  

 

 

 

Construction:

TEADIT style NA-1100 is a universal jointing sheet with high temperature and pressure resistance, manufactured from graphite and carbon fibre, bonded with Nitrile rubber (NBR). It is manufactured by means of a hot calender process under rigorous quality control standards which are registered  and certified under ISO 9001.

 

Application / service:

Style NA-1100 is suitable for sealing petroleum  derivatives, water, saturated steam, solvents         , gases and chemical products in general.   

          

Typical physical properties of NA-1100  

        ASTM test          Properties                           Values

F 36                   Compressibility                   9% F 36                   Recovery                           60% [pic 2]

        F 146                   Weight increse::

                                   5h/ASTM oil/Nr.3 @ + 150°C         10%

                                   5h/ASTM Fuel B @ +21-29°C         9 %

        F 146                   Thickness increase:

                           5h/ASTM oil/Nr. 3 @ +150°C         7%

                 5h/ASTM Fuel B @ +21-29°C         7%

        F 152                  Tensile strength (transverse)  17 N/mm²

        -                  Density                            1,7 g/cm³

 

Product standard:

thickness: 1,0 / 1,5 / 2,0 / 2,5 und 3,0 mm  sheet size: 1.500 x 1.600 mm, 1.500 x 3.200 mm

 

Approvals:

DVGW

KTW

 

 

Rev.Nr.: 04/110305

         

[pic 3] 

The P x T diagram above indicates the service limits for  NA-1100 considering the simultaneous influence of pressure and temperature (chemical suitability assumed). The green area represents the normal service limits, while the orange coloured area shows the maximum application limits. For those cases, please consult our technical department.